Surface Integrity of Dimethacrylate Composite Resins with Low Shrinkage Comonomers




Julkaisun tekijät: He Jingwei, Garoushi Sufyan, Säilynoja Eija, Vallittu Pekka K, Lassila Lippo

Julkaisuvuosi: 2021

Journal: Materials

Volyymi: 14

Julkaisunumero: 7

eISSN: 1996-1944

DOI: http://dx.doi.org/10.3390/ma14071614


Tiivistelmä

The goal of current research was to investigate the influence of adding low shrinkage "Phene" like comonomers hexaethylene glycol bis(carbamate-isoproply-α-methylstyrene) (HE-Phene) and triethylene glycol bis(carbamate-isoproply-α-methylstyrene) (TE-Phene) on the surface and color characteristics of composite resin. A range of weight fractions (0, 10, 20, 30, 40 wt.%) of HE/TE-Phene monomers were mixed with bisphenol A glycidyl methacrylate (GMA)/triethylene glycol dimethacrylate (TEGDMA) monomer. Experimental composite resins were made by mixing 71 wt.% of silica fillers to 29 wt.% of the resin matrix. A Vickers indenter and glossmeter were used for testing surface hardness (SH) and gloss (SG) at 60°. A chewing-simulator was used to evaluate the surface wear after 15,000 cycles. Color change (∆E) and translucency parameter (TP) were measured using a spectrophotometer. Data showed that HE/TE-Phene monomer had no negative impact (p > 0.05) on surface gloss, wear, color change and translucency of experimental composite resins. Surface hardness was in a reducing direction with the increas in HE/TE-Phene weight fraction (p < 0.05). The study results suggested that incorporating HE/TE-Phene monomers up to 30 wt.% with Bis-GMA/TEGDMA resin did not negatively influence the surface integrity of composite resins except for SH.


Ladattava julkaisu

This is an electronic reprint of the original article.
This reprint may differ from the original in pagination and typographic detail. Please cite the original version.




Last updated on 2021-24-06 at 09:07