Introduction: Erbium-doped yttrium-aluminum-garnet (Er:YAG) laser debonding of zirconia and lithium disilicate restorations is increasingly used for a range of clinical applications. Using rotary instruments to remove such restorations for any purpose has proven to be challenging. Erbium laser has been reported to be a conservative method for removing ceramic restorations. There is little data in the literature about the effect of adhesive resin cement type on the debonding time of the ceramic restoration using the Er:YAG laser.

Objectives: To evaluate and compare the time required for the Er:YAG laser to debond zirconia and lithium disilicate crowns bonded with a 2- and 1-bottle adhesive resin cement systems.

Materials and methods: Forty extracted premolar teeth were prepared and scanned for milled 40 CAD/CAM crowns. Teeth were randomly assigned into groups (n = 10 per group): 3 mol% yttria-partially stabilized zirconia crowns 3Y-PSZ (G1a) bonded with Panavia™ V5 (2-bottle adhesive resin cement), Zirconia 3Y-PSZ crowns (G1b) bonded with RelyX™ Ultimate (1-bottle adhesive resin cement), and for the lithium disilicate crowns bonded with the two types of cements (G2a, G2b). Each specimen was irradiated with an Er:YAG laser at 335 mJ, 15 Hz, 5.0 W, and 50-ms pulse duration (super short pulse mode). The irradiation time required for crowns to be successfully debonded was recorded for each specimen. Data were statistically analyzed using ANOVA and Tukey HSD post-hoc test (p < 0.05), at the 95 percent level of confidence. The intaglio surface of the debonded crown was analyzed using scanning electron microscopy (SEM).

Results: The mean ± standard deviation times needed for crown debonding were 5.75 ± 2.00 min for the G1a group, 4.79 ± 1.20 min for group G1b, 1.69 ± 0.49 min for group G2a, and 1.12 ± 0.17 for group G2b. There was no statistically significant difference in debonding time between the 2- and 1- bottle adhesive resin cement within the groups G1a and b (p = 0.2914), or between groups G2a b (p = 0.7116). A statistically significant difference (p < 0.05) was found between groups G1a and G2a and b and between groups G1b and G2a and b were SEM analysis showed no changes in the microstructure of the ceramic surface after Er:YAG laser irradiation.

Conclusion: Zirconia and lithium disilicate restorations can be debonded using Er:YAG lasers in a safe and efficient manner. There is no significant difference in the debonding time between the 2- and 1- bottle adhesive resin cement systems used in this study.

Clinical significance: Retrieving zirconia and lithium disilicate ceramics can be a challenging process when using diamond rotary instruments. ER:YAG lasers may efficiently debond these ceramics from the tooth structure, independent of the bonding process used for bonding them.