Microstructure and Mechanical Properties of Steel and Ni-Based Superalloy Joints for Rotors of High-Speed Electric Motors
Tekijät: Scherman Eero, Sikanen Eerik, Yeddu Hemantha Kumar, Amraei Mohsen, Sopanen Jussi
Kustantaja: MDPI
Julkaisuvuosi: 2022
Journal: Materials
Tietokannassa oleva lehden nimi: MATERIALS
Lehden akronyymi: MATERIALS
Artikkelin numero: 6906
Vuosikerta: 15
Numero: 19
Sivujen määrä: 18
eISSN: 1996-1944
DOI: https://doi.org/10.3390/ma15196906
Verkko-osoite: https://www.mdpi.com/1996-1944/15/19/6906
Rinnakkaistallenteen osoite: https://research.utu.fi/converis/portal/detail/Publication/176864037
High-speed electric motors, e.g., axially laminated anisotropic synchronous reluctance motors (ALA-SynRM), use a solid rotor manufactured by joining alternating layers of magnetic and non-magnetic metallic sheets. The strength of the dissimilar metallic joints is critical for the rotor's ability to withstand the operating conditions of the high-speed electrical machine. In this work, various dissimilar metallic joint configurations that can be used in high-speed ALA-SynRM rotors are studied by analyzing the shear strength, microstructure, hardness, and composition of the joints. Metallic joints of structural steels and Inconel (R) alloys fabricated by vacuum brazing and hot isostatic pressing (HIP) are studied. Finite element analysis (FEA) was performed to calculate the maximum shear stress of the joints that were subjected to various high speed operating conditions. The shear strength of the test specimens was measured and compared with FEA results. The microstructure and chemical composition of the joints were studied by using optical microscopy, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) on SEM. The results show that the hot isostatic pressed S1100MC-IN718 joint achieved the highest ultimate shear strength (233.3 MPa) followed by vacuum brazed S355MC-IN600 joint (230.1 MPa) and HIP S355-IN718 (203.5 MPa), thereby showing that vacuum brazing and HIP can be viable manufacturing methods to fabricate a high-speed ALA-SynRM rotor.