A1 Vertaisarvioitu alkuperäisartikkeli tieteellisessä lehdessä
Mechanical stability and technical outcomes of monolithic CAD/CAM fabricated abutment-crowns supported by titanium bases: An in vitro study
Tekijät: Pitta João, Hjerppe Jenni, Burkhardt Felix, Fehmer Vincent, Mojon Philippe, Sailer Irena
Kustantaja: WILEY
Julkaisuvuosi: 2021
Journal: Clinical Oral Implants Research
Tietokannassa oleva lehden nimi: CLINICAL ORAL IMPLANTS RESEARCH
Lehden akronyymi: CLIN ORAL IMPLAN RES
Vuosikerta: 32
Numero: 2
Aloitussivu: 222
Lopetussivu: 232
Sivujen määrä: 11
ISSN: 0905-7161
eISSN: 1600-0501
DOI: https://doi.org/10.1111/clr.13693(external)
Tiivistelmä
Objectives To evaluate mechanical stability (survival and complication rates) and bending moments of different all-ceramic monolithic restorations bonded to titanium bases (hybrid abutment-crowns) or to customized titanium abutments compared to porcelain-fused-to-metal crowns (PFM) after thermo-mechanical aging.
Material and Methods Sixty conical connection implants (4.3 mm-diameter) were divided in five groups (n = 12): PFM using gold abutment (GAbut-PFM), lithium disilicate crown bonded to customized titanium abutment (TAbut+LDS), lithium disilicate abutment-crown bonded to titanium base (TiBase+LDS), zirconia abutment-crown bonded to titanium base (TiBase+ZR), polymer-infiltrated ceramic-network (PICN) abutment-crown bonded to titanium base (TiBase+PICN). Simultaneous thermocycling (5°-55°C) and chewing simulation (1,200,000-cycles, 49 N, 1.67 Hz) were applied. Catastrophic and non-catastrophic events were evaluated under light microscope, and survival and complication rates were calculated. Specimens that survived aging were loaded until failure and bending moments were calculated.
Results Survival rates after aging were 100% (TAbut+LDS, TiBase+LDS), 91.7% (GA-PFM), 66.7% (TiBase+ZR) and 58.3% (TiBase+PICN) and differed among the groups (p = .006). Non-catastrophic events as screw loosening (GA-PFM) and loss of retention or micro-/macro-movement (TiBase groups) were observed. Complication rates varied among the groups (p < .001). TiBase+PICN had lower bending moment than all the other groups (p < .001).
Conclusions Hybrid abutment-crowns made of lithium disilicate can be an alternative to PFM-based restorations, although concerns regarding the bonded interface between the titanium base and abutment-crown can be raised. PICN and zirconia may not be recommended due to its inferior mechanical and bonding outcomes, respectively. Titanium customized abutment with bonded lithium disilicate crown appears to be the most stable combination.
Objectives To evaluate mechanical stability (survival and complication rates) and bending moments of different all-ceramic monolithic restorations bonded to titanium bases (hybrid abutment-crowns) or to customized titanium abutments compared to porcelain-fused-to-metal crowns (PFM) after thermo-mechanical aging.
Material and Methods Sixty conical connection implants (4.3 mm-diameter) were divided in five groups (n = 12): PFM using gold abutment (GAbut-PFM), lithium disilicate crown bonded to customized titanium abutment (TAbut+LDS), lithium disilicate abutment-crown bonded to titanium base (TiBase+LDS), zirconia abutment-crown bonded to titanium base (TiBase+ZR), polymer-infiltrated ceramic-network (PICN) abutment-crown bonded to titanium base (TiBase+PICN). Simultaneous thermocycling (5°-55°C) and chewing simulation (1,200,000-cycles, 49 N, 1.67 Hz) were applied. Catastrophic and non-catastrophic events were evaluated under light microscope, and survival and complication rates were calculated. Specimens that survived aging were loaded until failure and bending moments were calculated.
Results Survival rates after aging were 100% (TAbut+LDS, TiBase+LDS), 91.7% (GA-PFM), 66.7% (TiBase+ZR) and 58.3% (TiBase+PICN) and differed among the groups (p = .006). Non-catastrophic events as screw loosening (GA-PFM) and loss of retention or micro-/macro-movement (TiBase groups) were observed. Complication rates varied among the groups (p < .001). TiBase+PICN had lower bending moment than all the other groups (p < .001).
Conclusions Hybrid abutment-crowns made of lithium disilicate can be an alternative to PFM-based restorations, although concerns regarding the bonded interface between the titanium base and abutment-crown can be raised. PICN and zirconia may not be recommended due to its inferior mechanical and bonding outcomes, respectively. Titanium customized abutment with bonded lithium disilicate crown appears to be the most stable combination.