Synthesis of a novel tertiary amine containing urethane dimethacrylate monomer (UDMTA) and its application in dental resin

Julkaisun tekijät: Liu DL, Liu F, He JW, Lassila LVJ, Vallittu PK
Kustantaja: SPRINGER
Julkaisuvuosi: 2013
Journal: Journal of Materials Science: Materials in Medicine
Lehden akronyymi: J MATER SCI-MATER M
Numero sarjassa: 6
Volyymi: 24
Julkaisunumero: 6
ISSN: 0957-4530

A novel tertiary amine containing urethane dimethacrylate monomer UDMTA was synthesized with the aim of replacing Bis-GMA as one component of dental restorative materials. The structure of UDMTA was confirmed by FT-IR and H-1-NMR spectra. UDMTA was incorporated into Bis-GMA/TEGDMA (50 wt%/50 wt%) resin system to replace Bis-GMA partly and totally. Double bond conversion, polymerization volumetric shrinkage, water sorption and solubility, flexural strength and modulus of UDMTA containing resin formulations were studied with neat Bis-GMA/TEGDMA resin formulation as a reference. Results showed that UDMTA could be used as a coinitiator in photocurable dental resin, UDMTA containing resin had higher double bond conversion and lower polymerization shrinkage than that of Bis-GMA/TEGDMA resin, and the UDMTA containing copolymer had higher flexural strength and flexural modulus than Bis-GMA/TEGDMA copolymer. When UDMTA was used to replace more than 25 wt% of Bis-GMA, the obtained copolymer had higher water sorption and solubility. The optimized resin composition is by replacing 25 wt% of Bis-GMA in Bis-GMA/TEGDMA (50/50 by wt%), for the prepared resin had the best comprehensive properties.

Research Areas

Last updated on 2019-21-08 at 23:16